柚皮苷是中药骨碎补的主要活性成分,有促进成骨和骨组织新陈代谢的功能,目前载柚皮苷的羟基磷灰石/壳聚糖人工骨缓释材料未见报道.制备了壳聚糖(chitosan,CS)质量分数为10％,20％和30％的壳聚糖/羟基磷灰石-柚皮苷(chitosan/hydroxyapa-tite-naringin,CS/HA-N)缓释材料,并以 SEM、IR 和XRD 对材料进行了表征,同时研究了材料的机械性能、体外降解行为以及药物缓释行为.IR 和 XRD 结果表明,缓释材料的无机相为部分碳酸化的低结晶度羟基磷灰石,与天然骨相似.SEM 结果显示材料中羟基磷灰石(hydroxyapatite-N,HA)呈片状结晶.机械性能测试结果表明,缓释材料具有良好的力学性能, CS 含量为10％,20％和30％的 CS/HA-N 抗压强度分别为17．45±3．42,16．86±3．7和19．34±4．69 MPa.随着缓释材料中 CS 含量的增大,材料吸水率随之增大.体外缓释及体外降解行为研究结果表明,CS/HA对柚皮苷有良好的缓释效果,其药物释放速率以及降解速率随壳聚糖含量的增大而增大.CS/HA-N 作为载药人工骨替代材料具有良好的应用前景.
柚皮苷是中藥骨碎補的主要活性成分,有促進成骨和骨組織新陳代謝的功能,目前載柚皮苷的羥基燐灰石/殼聚糖人工骨緩釋材料未見報道.製備瞭殼聚糖(chitosan,CS)質量分數為10％,20％和30％的殼聚糖/羥基燐灰石-柚皮苷(chitosan/hydroxyapa-tite-naringin,CS/HA-N)緩釋材料,併以 SEM、IR 和XRD 對材料進行瞭錶徵,同時研究瞭材料的機械性能、體外降解行為以及藥物緩釋行為.IR 和 XRD 結果錶明,緩釋材料的無機相為部分碳痠化的低結晶度羥基燐灰石,與天然骨相似.SEM 結果顯示材料中羥基燐灰石(hydroxyapatite-N,HA)呈片狀結晶.機械性能測試結果錶明,緩釋材料具有良好的力學性能, CS 含量為10％,20％和30％的 CS/HA-N 抗壓彊度分彆為17．45±3．42,16．86±3．7和19．34±4．69 MPa.隨著緩釋材料中 CS 含量的增大,材料吸水率隨之增大.體外緩釋及體外降解行為研究結果錶明,CS/HA對柚皮苷有良好的緩釋效果,其藥物釋放速率以及降解速率隨殼聚糖含量的增大而增大.CS/HA-N 作為載藥人工骨替代材料具有良好的應用前景.
유피감시중약골쇄보적주요활성성분,유촉진성골화골조직신진대사적공능,목전재유피감적간기린회석/각취당인공골완석재료미견보도.제비료각취당(chitosan,CS)질량분수위10％,20％화30％적각취당/간기린회석-유피감(chitosan/hydroxyapa-tite-naringin,CS/HA-N)완석재료,병이 SEM、IR 화XRD 대재료진행료표정,동시연구료재료적궤계성능、체외강해행위이급약물완석행위.IR 화 XRD 결과표명,완석재료적무궤상위부분탄산화적저결정도간기린회석,여천연골상사.SEM 결과현시재료중간기린회석(hydroxyapatite-N,HA)정편상결정.궤계성능측시결과표명,완석재료구유량호적역학성능, CS 함량위10％,20％화30％적 CS/HA-N 항압강도분별위17．45±3．42,16．86±3．7화19．34±4．69 MPa.수착완석재료중 CS 함량적증대,재료흡수솔수지증대.체외완석급체외강해행위연구결과표명,CS/HA대유피감유량호적완석효과,기약물석방속솔이급강해속솔수각취당함량적증대이증대.CS/HA-N 작위재약인공골체대재료구유량호적응용전경.
Naringin was the main active ingredient in rhizoma drynariae,a traditional Chinese medicine herb, which has the function of promoting osteogenesis and bone metabolism.So far,Naringin loaded hydroxyapatite/chitosan composite for bone analogues has not been reported.In this paper,the chitosan/hydroxyapatite-naring-in (CS/HA-N)composite with 10%,20% and 30% chitosan contain were prepared.The samples were charac-terized by SEM,IR and XRD.Their mechanical properties,in-vitro release behavior and in-vitro degradation behavior were studied as well.The results showed that the crystals of this CS/HA-N composite containing car-bonate has low crystallinity,which was similar to natural bone.SEM results showed that the hydroxyapatite (hydroxyapatite-N,HA)presented plate shaped crystals.Mechanical performance test results showed that the material had good mechanical properties,the compressive strength of 10%,20%,30% CS/HA-N materials were 17.45±3.42,1 6.86±3.73,1 9.34±4.69 MPa,respectively.With chitosan content increasing in composite, water absorption rate of CS/HA-N was getting higher.The results of in-vitro release and in-vitro degradation test showed that CS/HA-N had good sustained release effect.The drug release rate and the degradation rate in-creased with the increase of chitosan content in CS/HA-N.CS/HA-N had good application prospect as drug de-livery systems for bone tissue engineering.