目的:探讨局部增粗的铸造桩对斜折单根牙固位力和抗折力的影响。方法收集新鲜拔除下颌第一前磨牙105颗,从牙冠颊侧釉牙骨质界冠方2 mm、舌侧釉牙骨质界根方2 mm截去牙冠,根管治疗后备用。取60颗牙随机分为4组,3组实验组分别在制作铸造桩时在桩的尖端增粗0.1 mm、0.2 mm和0.3 mm,对照组常规制作铸造桩。将桩加粘结剂敲击就位于对应的离体牙中,体视显微镜观察离体牙有无折裂,然后对无折裂离体牙进行拉力实验。取45颗牙分为3组,分别制作桩尖端增粗0.1 mm铸造桩、常规铸造桩和纤维桩,进行抗折实验。结果桩尖不增粗和增粗0.1 mm组无牙折裂,增粗0.2 mm和0.3 mm组均有牙折裂;桩尖不增粗组与增粗0.1 mm组的固位力有统计学差异(P=0.000),而抗折强度无统计学差异(P=0.134);两铸造桩组与纤维桩组抗折强度均有统计学差异(P=0.000)。结论铸造桩尖部增粗0.1 mm能增强斜折单根牙固位力,不增加牙折几率。
目的:探討跼部增粗的鑄造樁對斜摺單根牙固位力和抗摺力的影響。方法收集新鮮拔除下頜第一前磨牙105顆,從牙冠頰側釉牙骨質界冠方2 mm、舌側釉牙骨質界根方2 mm截去牙冠,根管治療後備用。取60顆牙隨機分為4組,3組實驗組分彆在製作鑄造樁時在樁的尖耑增粗0.1 mm、0.2 mm和0.3 mm,對照組常規製作鑄造樁。將樁加粘結劑敲擊就位于對應的離體牙中,體視顯微鏡觀察離體牙有無摺裂,然後對無摺裂離體牙進行拉力實驗。取45顆牙分為3組,分彆製作樁尖耑增粗0.1 mm鑄造樁、常規鑄造樁和纖維樁,進行抗摺實驗。結果樁尖不增粗和增粗0.1 mm組無牙摺裂,增粗0.2 mm和0.3 mm組均有牙摺裂;樁尖不增粗組與增粗0.1 mm組的固位力有統計學差異(P=0.000),而抗摺彊度無統計學差異(P=0.134);兩鑄造樁組與纖維樁組抗摺彊度均有統計學差異(P=0.000)。結論鑄造樁尖部增粗0.1 mm能增彊斜摺單根牙固位力,不增加牙摺幾率。
목적:탐토국부증조적주조장대사절단근아고위력화항절력적영향。방법수집신선발제하합제일전마아105과,종아관협측유아골질계관방2 mm、설측유아골질계근방2 mm절거아관,근관치료후비용。취60과아수궤분위4조,3조실험조분별재제작주조장시재장적첨단증조0.1 mm、0.2 mm화0.3 mm,대조조상규제작주조장。장장가점결제고격취위우대응적리체아중,체시현미경관찰리체아유무절렬,연후대무절렬리체아진행랍력실험。취45과아분위3조,분별제작장첨단증조0.1 mm주조장、상규주조장화섬유장,진행항절실험。결과장첨불증조화증조0.1 mm조무아절렬,증조0.2 mm화0.3 mm조균유아절렬;장첨불증조조여증조0.1 mm조적고위력유통계학차이(P=0.000),이항절강도무통계학차이(P=0.134);량주조장조여섬유장조항절강도균유통계학차이(P=0.000)。결론주조장첨부증조0.1 mm능증강사절단근아고위력,불증가아절궤솔。
Objective To explore the influence on retention force and fracture resistance of single root tooth with diagonal fracture when casting post was locally enlarged. Methods 105 mandibular first premolars newly extracted were gathered,with the decoronation from 2 mm above buccal cemento-enamel junction ( CEJ) to 2 mm under lingual CEJ prepared for the root canal therapy. 60 teeth were randomly assigned to 4 groups. In three experiment groups,the tips of casting posts were enlarged by 0. 1 mm,0. 2 mm,0. 3 mm respec-tively;in the control group,the posts were made by convention. Then all these posts were knocked into the corresponding teeth with lut-ing agent,fractures of the teeth were observed with stereomicroscope,and the tensile tests were made to those teeth with no fractures. The remaining 45 teeth were assigned to 3 groups,and conventional casting posts,casting posts with 0. 1 mm enlarged tip,and fiber posts were made respectively for fracture resistance tests. Then breaking-resistant tests were done. Results No fracture was found in the control group and the 0. 1 mm enlarged group,while in the 0. 2 mm,0. 3 mm enlarged groups,dental fractures were observed. There was statistical difference concerning retention force (P=0. 000),but no difference concerning fracture resistance (P=0. 134) between the control group and the 0. 1 mm enlarged group. There was statistical difference concerning fracture resistance between the two casting posts groups and the fiber posts group (P=0. 000). Conclusions The retention force of single root tooth with diagonal fracture can be enhanced with the casting posts when the tips were enlarged by 0. 1 mm,with no risk of dental fracture.