Fine low-silica iron ore tailing%Three-free brick%Admixture%Compressive strength%Water resistance
利用某种工业粉状废物制备廉价的无水泥固化剂,并以武钢矿业公司金山店铁矿细粒低硅铁尾矿为主要原料,研制MU25级的免烧、免蒸、免水泥建材砖(简称三免砖),考察了固化剂的掺量及其机械活化方式、试件的成型压力、化学外加剂种类及掺量、初期养护制度等工艺条件对制品抗压强度和耐水性的影响。试验结果表明:在成型压力为50 MPa条件下,混磨的固化剂掺量为25%,铁尾矿掺量为75%,有机早强剂A、防水剂B与固化剂掺量之比分别为0.02%、0.3%,初期养护温度为50℃、养护时间为36 h时,所制备的三免砖28 d的抗压强度和饱和抗压强度分别达到27.2 MPa和24.3 MPa,各项性能指标均能满足《JC/T422—2007非烧结垃圾尾矿砖》的要求。该研究为尾矿的大规模利用提供了一项投资小、效益高的技术。
利用某種工業粉狀廢物製備廉價的無水泥固化劑,併以武鋼礦業公司金山店鐵礦細粒低硅鐵尾礦為主要原料,研製MU25級的免燒、免蒸、免水泥建材磚(簡稱三免磚),攷察瞭固化劑的摻量及其機械活化方式、試件的成型壓力、化學外加劑種類及摻量、初期養護製度等工藝條件對製品抗壓彊度和耐水性的影響。試驗結果錶明:在成型壓力為50 MPa條件下,混磨的固化劑摻量為25%,鐵尾礦摻量為75%,有機早彊劑A、防水劑B與固化劑摻量之比分彆為0.02%、0.3%,初期養護溫度為50℃、養護時間為36 h時,所製備的三免磚28 d的抗壓彊度和飽和抗壓彊度分彆達到27.2 MPa和24.3 MPa,各項性能指標均能滿足《JC/T422—2007非燒結垃圾尾礦磚》的要求。該研究為尾礦的大規模利用提供瞭一項投資小、效益高的技術。
이용모충공업분상폐물제비렴개적무수니고화제,병이무강광업공사금산점철광세립저규철미광위주요원료,연제MU25급적면소、면증、면수니건재전(간칭삼면전),고찰료고화제적참량급기궤계활화방식、시건적성형압력、화학외가제충류급참량、초기양호제도등공예조건대제품항압강도화내수성적영향。시험결과표명:재성형압력위50 MPa조건하,혼마적고화제참량위25%,철미광참량위75%,유궤조강제A、방수제B여고화제참량지비분별위0.02%、0.3%,초기양호온도위50℃、양호시간위36 h시,소제비적삼면전28 d적항압강도화포화항압강도분별체도27.2 MPa화24.3 MPa,각항성능지표균능만족《JC/T422—2007비소결랄급미광전》적요구。해연구위미광적대규모이용제공료일항투자소、효익고적기술。
MU25 grade burning-free,autoclave curing-free and non-cement(“Three-free” for short) bricks were prepared by the fine low-silica iron ore tailing of Jinshandian Iron Mine,Wuhan Steel Mining Co. ,Ltd. ,as the main raw material,and the self-made non-cement made of industrial power waste as curing agent. The effect of the technical conditions such as dosage of curing agent and its mechanically milling facilities,molding pressure,the type and dosage of chemical admixture,the initial stage of curing regime on the compressive strength and water resistance of the products was investigated. The results show that the 28 d compressive strength and water absorption saturated compressive strength of the bricks can reach 27. 2 MPa and 24. 3 MPa respectively at conditions of forming pressure of 50 MPa,the curing agent of mixed grinding and the iron ore tailing of 25% and 75% respectively,dosage ratio of early strength agent A and waterproof ingagent B to curing agent of 0. 02% and 0. 3% respectively,early curing temperature of 50 ℃ and curing for 36 h. All properties meet the requirement in JC/T422-2007 standard“Unfired Bricks Made of Tailings”. The study provides a low investment and high profit technique for large scale utilization of such tailings.