含钛焊丝钢%TiN%连铸%析出%水口结瘤%工艺实践
含鈦銲絲鋼%TiN%連鑄%析齣%水口結瘤%工藝實踐
함태한사강%TiN%련주%석출%수구결류%공예실천
ER70S-G含钛焊丝钢(/%:0.07C,0.82Si,1.49Mn,0.012P,0.010S,0.19Ti,0.006 2N)生产流程为80 t顶底复吹转炉-LF-150mm× 150mm方坯连铸-盘条轧制工艺.热力学计算和生产实践表明,当浇铸温度≥1 560℃,[N]≤78.6×10-6,[Ti/%][N/%]≤0.001 49及拉速2.0~2.5 m/min时,可以避免在浇铸过程TiN析出和水口结瘤.
ER70S-G含鈦銲絲鋼(/%:0.07C,0.82Si,1.49Mn,0.012P,0.010S,0.19Ti,0.006 2N)生產流程為80 t頂底複吹轉爐-LF-150mm× 150mm方坯連鑄-盤條軋製工藝.熱力學計算和生產實踐錶明,噹澆鑄溫度≥1 560℃,[N]≤78.6×10-6,[Ti/%][N/%]≤0.001 49及拉速2.0~2.5 m/min時,可以避免在澆鑄過程TiN析齣和水口結瘤.