太原理工大学学报
太原理工大學學報
태원리공대학학보
Journal of Taiyuan University of Technology
2015年
6期
702-706
,共5页
张少华%高宜涛%寇晓辉%董晓强
張少華%高宜濤%寇曉輝%董曉彊
장소화%고의도%구효휘%동효강
水泥固化土%镉污染土%电阻率%无侧限抗压强度
水泥固化土%鎘汙染土%電阻率%無側限抗壓彊度
수니고화토%력오염토%전조솔%무측한항압강도
cement stabilized soil%cadmium contaminated soil%electrical resistivity%unconfined compressive strength
通过对水泥固化镉污染土进行电阻率和无侧限抗压强度试验,揭示了交流电频率对水泥固化镉污染土电阻率的影响,龄期和镉离子含量对水泥土电阻率和强度的影响规律以及电阻率与无侧限抗压强度的关系。结果表明:电阻率随电流频率的增加而明显降低,建议采用50 kHz~1 M Hz的电流测试频率范围;水泥土的强度及电阻率均随龄期的增加呈对数增加;当镉离子质量分数为50 mg/kg时,水泥土的强度和电阻率都达到最大值,随着镉离子质量分数的继续增加,强度和电阻率基本保持不变,且普遍高于无镉离子时的水泥土;水泥土强度同电阻率呈现出很好的线性关系。
通過對水泥固化鎘汙染土進行電阻率和無側限抗壓彊度試驗,揭示瞭交流電頻率對水泥固化鎘汙染土電阻率的影響,齡期和鎘離子含量對水泥土電阻率和彊度的影響規律以及電阻率與無側限抗壓彊度的關繫。結果錶明:電阻率隨電流頻率的增加而明顯降低,建議採用50 kHz~1 M Hz的電流測試頻率範圍;水泥土的彊度及電阻率均隨齡期的增加呈對數增加;噹鎘離子質量分數為50 mg/kg時,水泥土的彊度和電阻率都達到最大值,隨著鎘離子質量分數的繼續增加,彊度和電阻率基本保持不變,且普遍高于無鎘離子時的水泥土;水泥土彊度同電阻率呈現齣很好的線性關繫。
통과대수니고화력오염토진행전조솔화무측한항압강도시험,게시료교류전빈솔대수니고화력오염토전조솔적영향,령기화력리자함량대수니토전조솔화강도적영향규률이급전조솔여무측한항압강도적관계。결과표명:전조솔수전류빈솔적증가이명현강저,건의채용50 kHz~1 M Hz적전류측시빈솔범위;수니토적강도급전조솔균수령기적증가정대수증가;당력리자질량분수위50 mg/kg시,수니토적강도화전조솔도체도최대치,수착력리자질량분수적계속증가,강도화전조솔기본보지불변,차보편고우무력리자시적수니토;수니토강도동전조솔정현출흔호적선성관계。
The electrical resistivity and unconfined compressive strength of cadmium contaminated soil solidified by cement were measured ,to reveal the influence of AC frequency on electrical resistivity of the cadmium contaminated soil solidified by cement ;the influence law of age and cadmium ion content on resistivity and strength of cement soil ,and the relationship between the resistivity and unconfined com‐pressive strength .The results show that ,the electrical resistivity decreases significantly with the increase of current frequency ,and the range of 50 kHz~1 M Hz is recommended as the current testing frequency range .The compress strength and electrical resistivity of cemented soil increase logarithmically with age . When cadmium content is 50 mg/kg ,strength and resistivity reach the maximum ;As cadmium ion con‐tent continues to increase ,the resistivity and strength remain unchanged ,and generally higher than those of cemented soil without cadmium .Electrical resistivity and strength show a good linear relationship .