激光%硬化牙本质%微拉伸粘结强度
激光%硬化牙本質%微拉伸粘結彊度
격광%경화아본질%미랍신점결강도
laser%sclerotic dentin%micro-tensile bond strength
目的:比较2种不同激光对硬化牙本质与复合树脂粘接强度的影响。方法选择牙本质视觉分级3级以上牙面磨损的后牙30颗,按照随机数字表法随机分为Er,Cr:YSGG激光处理组( E组)、Nd:YAG激光处理组( N组)和对照组,联合Adper Prompt L-Pop处理、Z350复合树脂充填,置于37℃生理盐水中24 h,制作微拉伸试件并进行微拉伸粘接强度测试。采用SPSS13.0软件对微拉伸粘接强度值进行单因素方差分析。结果 E组粘接强度(24.71±3.13)MPa,N组粘接强度(21.72±2.36)MPa,对照组粘接强度(18.61±2.01)MPa。 E组的粘接强度最高,3组之间相比较差异均有统计学意义(P<0.05)。体视显微镜观察结果发现断裂多发生于牙本质-树脂粘接界面。结论 Er,Cr:YSGG激光和Nd:YAG激光均能够提高硬化牙本质与复合树脂的粘接强度,且Er,Cr:YSGG激光处理后获得的粘接强度更高。
目的:比較2種不同激光對硬化牙本質與複閤樹脂粘接彊度的影響。方法選擇牙本質視覺分級3級以上牙麵磨損的後牙30顆,按照隨機數字錶法隨機分為Er,Cr:YSGG激光處理組( E組)、Nd:YAG激光處理組( N組)和對照組,聯閤Adper Prompt L-Pop處理、Z350複閤樹脂充填,置于37℃生理鹽水中24 h,製作微拉伸試件併進行微拉伸粘接彊度測試。採用SPSS13.0軟件對微拉伸粘接彊度值進行單因素方差分析。結果 E組粘接彊度(24.71±3.13)MPa,N組粘接彊度(21.72±2.36)MPa,對照組粘接彊度(18.61±2.01)MPa。 E組的粘接彊度最高,3組之間相比較差異均有統計學意義(P<0.05)。體視顯微鏡觀察結果髮現斷裂多髮生于牙本質-樹脂粘接界麵。結論 Er,Cr:YSGG激光和Nd:YAG激光均能夠提高硬化牙本質與複閤樹脂的粘接彊度,且Er,Cr:YSGG激光處理後穫得的粘接彊度更高。
목적:비교2충불동격광대경화아본질여복합수지점접강도적영향。방법선택아본질시각분급3급이상아면마손적후아30과,안조수궤수자표법수궤분위Er,Cr:YSGG격광처리조( E조)、Nd:YAG격광처리조( N조)화대조조,연합Adper Prompt L-Pop처리、Z350복합수지충전,치우37℃생리염수중24 h,제작미랍신시건병진행미랍신점접강도측시。채용SPSS13.0연건대미랍신점접강도치진행단인소방차분석。결과 E조점접강도(24.71±3.13)MPa,N조점접강도(21.72±2.36)MPa,대조조점접강도(18.61±2.01)MPa。 E조적점접강도최고,3조지간상비교차이균유통계학의의(P<0.05)。체시현미경관찰결과발현단렬다발생우아본질-수지점접계면。결론 Er,Cr:YSGG격광화Nd:YAG격광균능구제고경화아본질여복합수지적점접강도,차Er,Cr:YSGG격광처리후획득적점접강도경고。
Objective To compare the effect of different kinds of lasers on micro-tensile bond strength of non-carious sclerotic den-tin.Methods Thirty human molars with occlusal wear were randomly divided into group E ,group N and the control group .Group E were treated with Er,Cr:YSGG laser,while group N were treated with Nd:YAG laser.Then all three groups were treated with Adper Prompt L-Pop,filled with Z350 resin,and preserved in normal saline (37 ℃)for 24 h.Then fatigue test pieces were made and the mi-cro-tensile bond strength was evaluated .Results were subject to statistical analysis using one-way analysis of variance (ANOVA).Re-sults The bonding strength was (24.71 ±3.13)MPa in group E,(21.72 ±2.36)MPa in group N,and (18.61 ±2.01)MPa in the control group.The differences among all groups were statistically significant (P<0.05).The breakage mostly happened in adhesive dentine surface .Conclusions The bonding strength of molars to Z 350 resin can be increased by Er ,Cr:YSGG laser and Nd:YAG la-ser,and the former is more effective .